Effect of Resin Cement System and Root Region on the Push-out Bond Strength of a Translucent Fiber Post

Objectives: This study evaluated the bond strength of luting systems for bonding glass fiber posts to root canal dentin. The hypothesis tested was that there are no differences in bond strength of glass fiber posts luted with different cement systems.Methods: Forty bovine incisors were randomly assigned to five different resin cement groups (n=8). After endodontic treatment and crown removal, translucent glass fiber posts were bonded into the root canal using five different luting protocols (self-cured cement and etch-and-rinse adhesive system; dual-cured cement and etch-and-rinse adhesive system; self-cured cement and self-etch adhesive system; dual-cured cement and self-etch adhesive system; and dual-cured self-adhesive cement). Push-out bond strength was evaluated at three different radicular levels: cervical, middle, and apical. The interface between resinous cement and the post was observed using a stereoscopic microscope.Results: Analysis of variance showed a statistically significant difference among the cements (p<0.05) and the root canal thirds (p<0.05). The self-adhesive resinous cement had lower values of retention.Conclusions: The resin cements used with etch-and-rinse and self-etch adhesive systems seem to be adequate for glass fiber post cementation.

Bond strength of different endodontic sealers to dentin: push-out test

Objective: The aim of this in vitro study was to evaluate the bond strength of different root canal sealers to dentin. Material and Methods: Forty extracted single-rooted human teeth were examined and the coronal and middle thirds of the canals were prepared with a 1.50 mm post drill (FibreKor Post System, Pentron). The teeth were allocated in two experimental groups, irrigated with 2.5% NaOCl+17% EDTA or saline solution (control group) and instrumented using Race rotary files (FKG) to a size #40 at the working length. Then, the groups were divided into four subgroups and filled with Epiphany sealer (Group 1), EndoREZ (Group 2), AH26 (Group 3) and Grossman's Sealer (Group 4). After 2 weeks of storage in 100% humidity at 37 degrees C, all teeth were sectioned transversally into 2-mm-thick discs. Push-out tests were performed at a cross-head speed of 1 mm/min using a universal testing machine. The maximum load at failure was recorded and expressed in MPa. Results: Means (+/- SD) in root canals irrigated with 2.5% NaOCl and 17% EDTA were: G1 (21.6 +/- 6.0), G2 (15.2 +/- 3.7), G3 (14.6 +/- 4.5) and G4 (11.7 +/- 4.1). Two-way ANOVA and Tukey's test showed the highest bond strength for the Epiphany's group (p < 0.01) when compared to the other tested sealers. Saline solution decreased the values of bond-strength (p < 0.05) for all sealers. Conclusion: Epiphany sealer presented higher bond strength values to dentin in both irrigating protocols, and the use of 2.5% NaOCl and 17% EDTA increased the bond strength values for all sealers.

Effect of adhesive system type and tooth region on the bond strength to dentin

Purpose: This study evaluated the bond strength of two etch-and-rinse adhesive systems (two- and three-step) and a self-etching system to Coronal and root canal dentin.Materials and Methods: The root canals of 30 human incisors and canines were instrumented and prepared with burs. The posts used for luting were duplicated with dual resin cement (Duo-link) inside Aestheti Plus #2 molds. Thus, three groups were formed (n = 10) according to the adhesive system employed: All-Bond 2 (TE3) + resin cement post (rcp) + Duo-link (DI); One-Step Plus (TE2) + rcp + DI; Tyrian/One-Step Plus (SE) + rcp + DI. Afterwards, 8 transverse sections (1.5 mm) were cut from 4 mm above the CEJ up to 4 mm short of the root canal apex, comprising coronal and root canal dentin. The sections were submitted to push-out testing in a universal testing machine EMIC (1 mm/min). Bond strength data were analyzed with two-way repeated measures ANOVA and Tukey's test (p < 0.05).Results: The relationship between the adhesives was not the same in the different regions (p < 0.05). Comparison of the means achieved with the adhesives in each region (Tukey; p < 0.05) revealed that TE3 (mean standard deviation: 5.22 +/- 1.70) was higher than TE2 (2.60 +/- 1.74) and SE (1.68 +/- 1.85).Conclusion: Under the experimental conditions, better bonding to dentin was achieved using the three-step etch-and-rinse system, especially in the coronal region. Therefore, the traditional etch-and-rinse three-step adhesive system seems to be the best choice for teeth needing adhesive endodontic restorations.

The Disk-Specimen Thickness Does Not Influence the Push-Out Bond Strength Results Between Fiber Post and Root Dentin

This study evaluated the effect of different thickness of disk-shaped specimens on the push-out bond strength test. Eighteen lower bovine teeth were sectioned (20mm) and prepared (15mm) with the same post system drill (Light Post (R) #1, Schaumburg, IL, Bisco, USA). The apical third of each specimen was embedded in a plastic matrix filled with an acrylic resin (Dencrilay (TM), Dencril, São Paulo, Brazil). The posts were cleaned with alcohol, silanated (ProSil (R), FGM, Joenville, SC, Brazil) and cemented with the RelyX (TM) U100 (3M ESPE, St. Paul, MN, USA). Each specimen was sectioned into three pieces of differing thicknesses (1, 2, and 4 mm). These disk-samples were allocated into 3 groups (n=18) and subjected to push-out testing. One-way ANOVA showed no influence of the specimen thickness on the results (p=0.842). No correlation was observed between thickness and push-out bond strength (Pearson Correlation, r(2)=0.0688; P=0.6209). The push-out bond strength test was not affected by the thickness of the disk-specimens.

Comparison of resin push-out strength to root dentin of bovine- and human-teeth

Aim : To compare the push-out strength of bovine- and human-root dentin and, thus, evaluate the suitability of bovine-root dentin to substitute human-root dentin for bond strength testing. Materials and Methods : Ten single-rooted human-teeth and ten bovine incisors were prepared using a #3 bur of a fiber post system (12 mm long). The posts were duplicated with resin cement (Duolink). The root canals were treated with All Bond 2 adhesive system and the resin posts were cemented using Duolink. The specimens were cut perpendicular to their long axis, yielding disc-specimens with 1.5 mm thickness, which were submitted to a push-out test (1 mm/min). Ten bond strength values per group (n = 10) were used for statistical analysis (Student t test, a =.05). Results : Statistically significant differences were found for the bond strength values between bovine- (4.1 1.3 MPa) and human-root dentin (8.6 5.7 MPa) (P =.0001). Conclusion : The push-out strengths of bovine- and human-root dentin were statistically different.

Effect of light-curing units on push-out fiber post bond strength in root canal dentin

The purpose of this study was to evaluate the effectiveness of different light-curing units on the bond strength (push-out) of glass fiber posts in the different thirds of the root (cervical, middle and apical) with different adhesive luting resin systems (dual-cure total-etch; dual-cured and self-etch bonding system; and dual-cure self-adhesive cements), Disks of the samples (n = 144) were used, with approximately 1 mm of thickness of 48 bovine roots restored with glass fiber posts, that were luted with resin cements photo-activated by halogen LCU (QTH, Optilux 501) and blue LED (Ultraled), with power densities of 600 and 550 mW/cm 2, respectively. A universal testing machine (MTS 810 Material Test System) was used with a 1 mm diameter steel rod at cross-head speed of 0.5 mm/min until post extrusion, with load cell of 50 kg, for evaluation of the push-out strength in the different thirds of each sample. The push-out strength values in kgf were converted to MPa and analyzed through Analysis of Variance and Tukey's test, at significance level of 5%. The results showed that there were no statistical differences between the QTH and LED LCUs. The self-adhesive resin cement had lower values of retention. The total-etch and self-adhesive system resin cements seem to be a possible alternative for glass fiber posts cementation into the radicular canal and the LED LCU can be applied as an alternative to halogen light on photo-activation of dual-cured resin cements. © 2009 Pleiades Publishing, Ltd.

Multi-step adhesive cementation versus one-step adhesive cementation: push-out bond strength between fiber post and root dentin before and after mechanical cycling

This study evaluated the effects of mechanical cycling on resin push-out bond strength to root dentin, using two strategies for fiber post cementation. Forty bovine roots were embedded in acrylic resin after root canal preparation using a custom drill of the fiber post system. The fiber posts were cemented into root canals using two different strategies (N = 20): a conventional adhesive approach using a three-step etch-and-rinse adhesive system combined with a conventional resin cement (ScotchBond Multi Purpose Plus + RelyX ARC ), or a simplified adhesive approach using a self-adhesive resin cement (RelyX U100). The core was built up with composite resin and half of the specimens from each cementation strategy were submitted to mechanical cycling (45 degree angle; 37 degrees C; 88 N; 4 Hz; 700,000 cycles). Each specimen was cross-sectioned and the disk specimens were pushed-out. The means from every group (n = 10) were statistically analyzed using a two-way ANOVA and a Tukey test (P = 0.05). The cementation strategy affected the push-out results (P < 0.001), while mechanical cycling did not (P = 0.3716). The simplified approach (a self-adhesive resin cement) had better bond performance despite the conditioning. The self-adhesive resin cement appears to be a good option for post cementation. Further trials are needed to confirm these results.